| Term |
To convert from |
To be multiplied by |
| Magnetic flux density B |
Tesla ( Wb/m2 ) to Gauss |
104 |
| Gauss to Tesla ( Wb/m2 ) |
10- 4 |
| Magnetic field strength H |
Ampere-turns/meter to Oersted |
0.0126 |
|
Oersted to Ampere-turns/meter |
79.6 |
| Ampere-turns/meter to Ampere-turns/inch |
0.0254 |
|
Ampere-turns/meter to Ampere-turns/cm |
0.01 |
| Core
Loss |
Watt/Kg to Watt/pound |
0.4536 |
|
Watt/pound to Watt/Kg |
2.205 |
| Watts/Kg at 60Hz(1.5T)to Watts/Kg at 50Hz(1.5T) |
0.75 for GO, 0.79 for CRNGO |
|
Watts/lb at 60Hz(1.5T)to Watts/Kg at 50Hz(1.5T) |
(approximate)1.65 for GO, 1.74 for CRNGO |
| Length / |
Centimeter to inch |
0.3937 |
| Inch to centimeter |
2.54 |
| Area
A |
Square cm to Square inch |
0.155 |
| Square inch to Square cm |
6.45 |
| Volume V |
cm3 to cubic inch |
0.061 |
| cubic inch to cm3 |
16.4 |
| Mass m |
gm to Ounce |
0.0353 |
|
Kg to pound |
2.205 |
| Ounce to gm |
28.35 |
| Pound to Kg |
0.4536 |
| Tensile strength R |
N/mm2 to Kg/mm2 |
0.102 |
| Kg/mm2 to N/mm2 |
9.81 |
| Temperature T |
°C to °F |
X 1.8 +32 |
| °F to °C |
X 0.556 17.8 |